Hidrogéis Superabsorventes a Base de Acetato de Celulose Modificado por Dianidrido 3, 3’, 4, 4’ Benzofenona Tetracarboxílico (BTDA): Síntese, Caracterização e Estudos Físico-Químicos de Absorção

Synthesis of Hydrogels of Cellulose Acetate (AC) Cross-Linked With 3,3’,4,4’ Benzophenonetetracarboxylic Dianhydride (BTDA): Characterization and Adsorption Physicochemical Study

Oliveira, Victor A.; Santos, Cláudio G.; Botaro, Vagner R.

Downloads: 2
Views: 387

Resumo

2. Petrus, J. C. C. - "Preparação, modificação e caracterização de membranas assimétricas para clarificação de suco de frutas", Tese de Doutorado, Universidade Estadual de Campinas, São Paulo, Brasil (1997). 3. Sysel, P.; Sindelar, V.; Kubonova, M.; Friess, K.; Hynek, V. & Sipek, M. - Desalination, 236, p.46 (2009). 4. Basseti, F. J. - "Preparação, caracterização e aplicação de membranas poliméricas microporosas assimétricas", Tese de Doutorado, Universidade Estadual de Campinas, São Paulo, Brasil (2002). 5. Sinha Ray, S. & Okamoto, M. - Poly. Sci., 28, p.1539 (2003). 6. Pinna vaia, T. J. & Beall, G. W. - "Polymer-Clay Nanocomposites", John Wiley & Sons, Toronto (2000). 7. P az, R. A.; Leite, A. M. D.; Araujo, E. M.; Melo, T. J. A.; Barbosa, R. & Ito, E. N. - Polímeros: Ciência e Tecnologia, 18, p.341 (2008). 8. Espeso, J.; Lozano, A. E.; Campa, J. G. & Abajo, J. - J. Membr. Sci., 280, p.659 (2006). 9. Messersmith, P. B. & Giannelis, E. P. - J. Polym. Sci., 33, p.1047 (1995). 10. Chang, J. H.; An, Y. U. & Sur, G. S. - J. Polym. Sci., 41, p.94 (2003). 11. Gain, O.; Espuche, E.; Pollet, E.; Alexandre, M. & Dubois, P. H. - J. Polym. Sci., 43, 2, p.205 (2005). 12. Ranade, A.; D’Souza, N. A.; Gnade, B.;Este trabalho descreve as sínteses de hidrogéis superabsorventes a base de acetato de celulose (AC), com grau de substituição 2.5, reticulado com dianidrido 3, 3’, 4, 4’ benzofenona tetracarboxílico (BTDA). As caracterizações das matérias primas foram realizadas por análises térmicas (TG/DTG) e espectroscopia na região do infravermelho (FTIR). O grau de substituição do acetato de celulose foi determinado por via úmida. A confirmação da reação de esterificação foi possível a partir da técnica de FTIR, espectroscopia UV-vis e análises térmicas (TG/DTG). A presença de poros no novo material foi analisada por microscopia eletrônica de varredura (MEV) e porosimetria (BET). A influência da concentração de dianidrido no meio reacional foi investigada, bem como a influência do aumento no grau de reticulação no comportamento térmico do material. Foram obtidas isotermas de absorção de água em diferentes temperaturas para os hidrogéis com diferentes graus de reticulação. Os coeficientes de difusão dos géis foram determinados, juntamente com a energia de ativação para o processo de inchamento usando a equação de Arrhenius. A entalpia de mistura do sistema gel-água foi determinada pela medida da quantidade máxima de água absorvida no equilíbrio a diferentes temperaturas, empregando a equação de Gibbs/Helmholtz. Dharia, A. - J. Plastic Film Sheeting, 19, p.271 (2003).

Palavras-chave

Hidrogéis, acetato de celulose, entalpia de mistura

Abstract

This work describes the synthesis of hydrogels of cellulose acetate (AC), with a nominal degree of substitution DS = 2.5, cross-linked with 3,3’,4,4’ benzophenonetetracarboxylic dianhydride (BTDA). The raw materials were characterized by thermal analysis (TG/DTG) and by Fourier transform infrared spectroscopy (FTIR). DS of cellulose acetate was determined by titration with a known amount of standard NaOH solution. Hydrogels of BTDA were synthesized with 0.5, 0.75 and 1.0 mol of BTDA/mol of AC. FTIR proved to be a suitable method to monitor the course of reactions and the progress of purification. UV-vis spectroscopy and analysis confirmed the esterification of the free hydroxyl groups. Surface modification of AC structure after the cross-linking reaction was analyzed by Scanning Electron Microscope (SEM) and density and porosity of the hydrogels were determined by BET. The influence of the concentration of dianhydride on the time necessary for formation of the gel was investigated. The influence from the increase in the degree of cross-linking on the thermal behavior of the material was also documented. Water absorption isotherms were obtained for hydrogels with different reticulating agents and reticulation degrees at different temperatures. The Arrhenius equation was used to determine the diffusion coefficient of the different hydrogels at distinct temperatures and the threshold energy for the swelling process. The enthalpy of mixture was determined through the measurement of the maximum quantity of water absorbed at equilibrium at different temperatures, with the Gibbs/Helmholtz equation.

Keywords

Hydrogels, cellulose acetate, enthalpy of mixture

References

1. Oliveira Júnior, A. R. - “Obtenção e caracterização de acetato de celulose modificado com organossilano”, Tese de Doutorado, Universidade Estadual de Campinas, Brasil (2002).

2. Singh, B.; Chauhan, G. S. S. & Nirmala Chauhan, K. - Carbohydrate Polymers, 67, p.190 (2002).

3. El-hag Ali, A.; Shawky, H. A.; Abd El Rehim, H. A. & Hegazy, E. A. - European Polymer Journal, 39, p.2337 (2003).

4. Karadag, E.; Saraydin, D. & Güven, O. - NIMB Beam Interactions with Materials & Atoms, 225, p.489 (2004).

5. Jabbari, E. & Nozari, S. - European Polymer Journal, 36, p.685 (2000).

6. Kioussis, D. R. & Kofinas, P. - Polymer, 46, p.10167 (2005).

7. Gocho, H.; Shimizu, H.; Tanioka, A.; Chou, T. J. & Nakajima, T. - Carbohydrate Polymers, 41, p.83-86 (2000).

8. Ende, M. T. & Peppas, N. A. - Journal of controlled release, 48, p.47 (1997).

9. Peppas, N. A. & Khare, A. R. - Advanced Drug Dellivery Reviews, 11, p.1 (1993).

10. Peniche, C.; Cohen, M. E.; Vázquez, B. & San Román, J. - Polymer, 38, p.5977 (1997).
588371587f8c9d0a0c8b485d polimeros Articles
Links & Downloads

Polímeros: Ciência e Tecnologia

Share this page
Page Sections