Adsorção de Fibronectina a Arcabouços de Polihidroxibutirato Aplicáveis à Engenharia Óssea

Adsorption of Fibronectin onto Polyhydroxybutyrate Scaffolds Applied to Bone Engineering

Mendonça, Roberta H.; Thiré, Rossana M. S. M.; Costa, Marysilvia F. da; Filho, Fernando C. S.

Downloads: 0
Views: 242

Resumo

Fibronectina sérica humana foi adicionada à superfície de arcabouços de polihidroxibutirato (PHB) a fim de otimizar a adesão de osteoblastos humanos (HOB). Visando a criar sítios para a imobilização de fibronectina (FN), os arcabouços foram previamente tratados por meio de reação com etilenodiamina. O tratamento modificou a morfologia e a composição química dos arcabouços, possibilitando um aumento no teor de FN adsorvido à superfície. Imagens de AFM mostraram que as moléculas de FN assumiram conformações distintas, de acordo com a superfície na qual foi imobilizada. A FN adicionada aos arcabouços não modificados possivelmente assumiu uma conformação estendida, expondo os grupamentos RGD. Com isso, houve um aumento na adesão de HOB a estes materiais. Por outro lado, a FN na superfície dos arcabouços previamente tratados possivelmente apresentou-se na forma compacta, suprimindo a adesão de HOB.

Palavras-chave

Polihidroxibutirato, engenharia óssea, biomateriais, modificação de superfície

Abstract

Human plasma fibronectin (FN) was adsorbed onto the surface of polyhydroxybutyrate (PHB) scaffolds with aim of improving adhesion of human osteoblasts (HOB). PHB scaffolds were modified via reaction with ethylenediamine in order to create sites for FN immobilization. Morphological and chemical composition changes were observed for treated scaffolds which led to an increase in the concentration of FN adsorbed onto scaffold surfaces. AFM images showed that FN molecules assumed distinct conformation according to the surface to which they were adsorbed. It is believed that the FN molecules added to non-treated scaffolds assumed an unfolded conformational owing to the exposure of their RGD domains, thus promoting an increased HOB adhesion. On the other hand, FN molecules which were added to the surface of previously treated scaffolds are believed to have assumed a folded conformation, hiding some RGD domains and inhibiting HOB adhesion.

Keywords

Polyhydroxybutyrate, bone engineering, biomaterials, surface modification

References

1. Meijer, G. J.; Bruijn, J. D.; Koole, R. & Blitterswijk, C. A. - Plos Med., 4, p.260 (2007).

2. Hutmacher, D. W. - Biomaterials, 21, p.5960 (2000).

3. Sánchez-Salcedo, S.; Nieto, A. & Vallet-Regí M. - Chem. Eng. J., 137, p.62 (2008).

4. Kai, Z.; Ying, D. & Chen, G. Q. - Bioch. Eng. J., 16, p.115 (2003).

5. Lorcan, T. A.; Tosetto, M.; Miller, I. A.; O’Connor, D. P.; Penney, S. C.; Lynch, I.; Keenan, A. K.; Pennington, S. R.; Dawson, K. A. & Gallagher W. M. - Biomaterials, 27, p.3096 (2006).

6. Thiré, R. M. S. M.; Meiga, T.O; Dick, S. & Andrade, L.R. - Macromol. Symp., 258, p.38 (2007).

7. Yang, X.; Zhao, K. & Chen, G. Q. - Biomaterials, 23, p.1391 (2002).

8. Costa, F. S. & Mendes, G. C. - Mater. Sci. Eng., 24, p.637 (2003)

9. Zhang, Y.; Chai, C. & Jiang, X. S. - Mater. Sci. Eng. C, 27, p.213 (2007).

10. Zhu, Y.; Gao, C.; Liu, X. & Shen, J. - Biomacromol., 3, p.1312, (2002).

11. Holländer, A.; Thome, J.; Keusgen, M.; Degener, I. & Klein, W. - Appl. Surf. Sci., 235, p.145 (2004).

12. Rouxhet, L.; Duhoux, F.; Borecky, O.; Legras, R. & Schneider, Y. J. - J. Biomater. Sci. Polym., 12, p.1279 (1998).

13. Sader, M. S.; Ferreira, M. & Dias, M. L. - Polímeros: Cienc. Tecnol., 16, p.12 (2006).

14. Bradford, M. M. - Anal. Biochem., 72, p.248, (1976).

15. Ito, Y. et al. - Biomaterials, 18, p.197, (1997).

16. Shin, H. et al. - Biomaterials, p.126, (2006).
5883712d7f8c9d0a0c8b477e polimeros Articles
Links & Downloads

Polímeros: Ciência e Tecnologia

Share this page
Page Sections