Compósitos de Borracha Natural ou Policloropreno e Celulose II: Influência do Tamanho de Partícula

Natural Rubber or Chloroprene Rubber and Cellulose II Composites: Influence of Particle Size

Suarez, João Carlos Miguez; Nunes, Regina Célia R.; Visconte, Leila L. Y.; Martins, Agnes F.; Napolitano, Bruno de A.

Downloads: 0
Views: 242

Resumo

O objetivo deste trabalho foi o desenvolvimento de compósitos claros com propriedades de interesse tecnológico utilizando elastômeros com diferentes polaridades. Para que este objetivo fosse atingido, celulose II em pó foi usada como carga, em borracha natural (NR) ou policloropreno (CR). A celulose II foi obtida por coagulação da solução de xantato de celulose em meio ácido, sob agitação constante e à temperatura ambiente, constituindo uma nova forma de obtenção deste tipo de carga. Compósitos com 10 phr de celulose II com NR e CR, respectivamente, foram desenvolvidos tendo como variável o tamanho de partícula da carga. As propriedades mecânicas e os aspectos microscópicos dos diferentes compósitos foram avaliados e comparados com aqueles das formulações sem carga. Os resultados permitiram identificar o compósito como o de melhor resultado, influenciado pela polaridade da matriz elastomérica e pelo tamanho de partícula da carga, conseqüência das condições de moagem usadas.

Palavras-chave

Borracha natural, policloropreno, celulose II, propriedades mecânicas, microscopia eletrônica de varredura

Abstract

The aim of this work was to develop light composites with properties of technological interest by using elastomers of different polarities. This was achieved by employing cellulose II, in the powder form, as filler in natural rubber (NR) and chloroprene (CR). Cellulose II was obtained by coagulation of cellulose xanthate solution, in acid medium, under stirring and at room temperature, which represents, to our knowledge, a new way of obtaining this type of filler. Composites with 10phr of cellulose II and NR or CR were prepared having the particle size as variable. The mechanical properties and the microscopic aspect of the different composites were evaluated and compared with compounds without filler. The results indicated best results for the CR composite, influenced by the polarity of the elastomeric matrix and by the particle size, as a consequence of the milling conditions of the filler used.

Keywords

Natural rubber, chloroprene rubber, cellulose II, mechanical properties, scanning electron microscopy

References



1. Dannenberg, E.M. - Rubber Chem. Technol., 48, p.411 (1975)

2. Boonstra, B.B. – Polym., 20, p.691 (1979)

3. Medalia, A.I. & Kraus, G. - “Reinforcement of Elastomers by Particulate Fillers”, in: Science and Technology of Rubber, cap.8, Second Edition, Academic Press, New York (1995)

4. Bokobza, L. & Rapoport, O. - J. Appl. Polym. Sci., 85, p.2301 (2002)

5. Leblanc, J. L. - Prog. Polym. Sci., 27, p.627 (2002)

6. Suarez, J. C. M. - “Influência da radiação gama no comportamento na fratura de mistura de polietilenos reciclados”, Tese de Doutorado, Universidade Federal do Rio de Janeiro, Brasil (1999)

7. Martins, A. F.; Meneses, S. M.; Visconte, L. L. Y. & Nunes, R. C. R. - J. Appl. Polym. Sci., 92, p.2425 (2004)
588370fc7f8c9d0a0c8b4686 polimeros Articles
Links & Downloads

Polímeros: Ciência e Tecnologia

Share this page
Page Sections