Vanin, Mirela; Santana, Cesar C.; Torriani, Íris L.; Privelic, Tomás; Duek, Eliana Ap. R.

doi:10.1590/S0104-14282004000300015

Scientific & Technical Article

Estudo da Degradação "In Vitro" de Blendas de Poli(β-Hidroxibutirato) (PHB)/Poli(L-Ácido Latico) (PLLA) na Forma de Filmes

In Vitro Study of Degradation of Poly(ß-Hydroxybutyrate) (PHB) / Poly(L-Lactic Acid) (PLLA) Blends in the Form of Films

Vanin, Mirela; Santana, Cesar C.; Torriani, Íris L.; Privelic, Tomás; Duek, Eliana Ap. R.

http://dx.doi.org/10.1590/S0104-14282004000300015 Polímeros: Ciência e Tecnologia, vol.14, n3, p.187-193, 2004

PDF

Downloads: 0

Resumo

Neste trabalho foi realizado um estudo de avaliação da degradação “in vitro” da blenda biorreabsorvível poli(β- hidroxibutirato) (PHB) / poli(L-ácido lático) (PLLA). As blendas PHB/PLLA na forma de filmes, nas composições 0/100, 30/70, 50/50, 70/30 e 100/0 (% em massa), foram obtidas pelo método de evaporação do solvente. Os filmes obtidos foram imersos em solução tampão fosfato salino, PBS, (pH 7,4) por 12 meses em banho termostatizado à 37°C. As amostras foram caracterizadas por MDSC, TG, DMA, SEM, WAXS e SAXS, antes e após o processo de degradação. Os resultados mostraram que a blenda PHB/PLLA é imiscível em todas as composições estudadas, apresentando morfologia com separação de fases. Observou-se que o PLLA perdeu propriedades mecânicas de tração mais rapidamente que o PHB, durante o processo de degradação, tornando-se mais quebradiço. Verificou-se também aumento no grau de cristalinidade e na espessura do período longo das cadeias poliméricas nas blendas em função da degradação, sugerindo aumento da lamela cristalina.

Palavras-chave

Blendas, polímeros biorreabsorvíveis, biomateriais, poli(β-hidroxibutirato) (PHB), poli(L-ácido lático) (PLLA)

Abstract

In this work, “in vitro” degradation of poly(β-hydroxybutyrate) (PHB) / poly(L-lactic acid) (PLLA) blends was evaluated. Films of PHB/PLLA blends, in the compositions 0/100, 30/70, 50/50, 70/30 and 100/0 (% weight), were fabricated by casting. The films obtained were immersed in a phosphate buffer solution, PBS (pH 7.4) for 12 months. The samples were characterized by MDSC, TG, DMA, SEM, WAXS and SAXS, before and after the degradation process. The results showed that the PHB/PLLA blends are immiscible and present phase separation as indicated by microscopy. The PLLA loses mechanical properties faster than PHB, during the degradation process. It was observed that the blends increased their crystallinity degree and long period thickness as a function of degradation time.

Keywords

Blends, bioreabsorbable polymers, biomaterials, poly(β,-hydroxybutyrate) (PHB) and poly(L-lactic acid) (PLLA

References

1. Yuehuei, H. A.; Shane K. W.; Richard, J. F. – Biomaterials, 21, p.2635 (2000).

2. Ferreira, B. M. P.; Zavaglia, C. A. C.; Duek, E. A. R. - Materials Research, 4, p.34 (2001).

3. Kimura, Y. – “Biodegradable Polymers”, in: Biomedical Applications of Polymeric Materials. p. 163-189, CRC Press (ed.), EUA (1993).

4. Zhang, L.; Xiong, C.; Deng, X. – J Appl Polym Sci, 56, p.103 (1995).

5. Ignatius, A. A.; Claes, L. E. – Biomaterials, 17, p.831 (1996).

6. Elst, M. V. - J Biomed Mater Res, 30, p.139 (1996).

7. Duek, E. A. R.; Zavaglia, C. A. C.; Belangero, W. D. - Polymer, 40, p.6465 (1999).

8. Reis, R. L.; Cunha, A. M. – J. Mat. Sci.: Materials in Medicine, 6, p.786 (1995).

9. Park, S. H.; Lim, S. T.; Shin, T. K.; Choi, H. J.; Jhon, M. S. – Polymer, 42, p.5737 (2001).

10. Middleton, J. C.; Tripton, A. J. – Biomaterials, 21, p.2335 (2000).

11. Wake, M.C.; Gerecht, P. D.; Lu, L.; Mikos, A. G. - Biomaterials, 19, p.1255 (1998).

12. Ferreira, B. M. P. – “Obtenção, Caracterização, Estudo “In Vitro”e “In Vivo”de Blendas de Poli(L-ácido láctico) / Poli(hidroxibutirato-co-hidroxivalerato)”, Tese de Doutorado, Universidade Estadual de Campinas, Brasil (2002).

13. Koyama, N.; Dói, Y. – Can J Microbiol, 41, p.316 (1995).