Propriedades térmicas e mecânicas dos compósitos de Polipropileno pós-consumo reforçados com fibras de celulose

Thermal and mechanical properties of post-consumer polypropylene composites reinforced with cellulose fibers

Spadetti, Carolini; Silva Filho, Eloi Alves da; Sena, Geovane Lopes de; Melo, Carlos Vital Paixão de
Abstract:
Foram investigadas as propriedades térmicas e mecânicas de compósitos de polipropileno reciclado e virgem, reforçados com até 40% em peso de fibras de celulose (FC), bem como a morfologia da matriz polimérica. Para a obtenção dos dados, foram utilizadas as técnicas de Análise Témica Dinâmico-Mecânica (DMTA), Calorimetria Exploratória Diferencial (DSC) e Microscopia Eletrônica de Varredura (MEV). Os resultados mostraram que os compósitos de polipropileno reciclado,com percentagem de 30% FC e os compósitos de polipropileno virgem, com percentagem de 20% FC, tiveram um aumento significativo nos valores de módulo de armazenamento (E') e grau de cristalinidade (χc), indicando com isso uma resistência mecânica mais elevada. Já nas amostras com 40% FC, houve uma diminuição na rigidez do material. Estes resultados foram confirmados por MEV, onde observou-se a aglomeração das fibras de celulose na matriz. Não houve alteração nas temperaturas de transição vítrea (Tg) e fusão cristalina (Tm) dos compósitos produzidos.
Abstract:
The thermal and mechanical properties of composite recycled and virgin of polypropylene were investigated, reinforced with up to 40% by weight of cellulose fibers (FC), as well as the morphology of the polymer matrix. To obtain the data, techniques for Dynamic-Mechanical Thermal Analysis (DMTA) were used, Differential Scanning Calorimetry (DSC) and Scanning Electron Microscopy (SEM). The results showed that recycled polypropylene composites with a percentage of 30% FC and virgin polypropylene composites with a percentage of 20% FC had a significant increase in storage modulus values (E') and degree of crystallinity (χc), indicating a higher mechanical strength in these composites. Since the samples with 40% FC, there was a decrease in the stiffness of the material. These results were confirmed by the SEM, where noted agglomeration of the cellulose fibers in the matrix. There was no change in the glass transition temperature (Tg) and crystalline melting temperature (Tm) of the produced composite.
Keywords:
compósitos de polipropileno, fibras de celulose, compósitos pós-consumo.
Keywords:
polypropylene composite, cellulose fibers, post consumer composite.